Densified foam for thermal insulation in electronic devices

ABSTRACT

A heat spreading and insulating material using densified foam is provided that has a heat spreading layer that is adhered to an insulating layer. The material is designed to be used with mobile devices that generate heat adjacent to heat sensitive components. The insulating layer is formed from a compressed layer of polyimide foam to increase its density. The polyimide foam retains a significant amount of insulating properties through the densification process. In some embodiments, an EMI shielding layer is added to improve electrical properties of the device. The heat spreading layer may be a graphite material with heat conducting properties that preferentially conduct heat in-plane but can also be metal foil or other isotropic heat conducting material. The material may also include pressure sensitive layers to permanently apply the material to the mobile device.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Utility application Ser. No.15/357,800, filed Nov. 11, 2016, which claims the benefit of U.S.Provisional Application No. 62/257,307, filed Nov. 19, 2015, thedisclosures of which are hereby incorporated by reference.

BACKGROUND OF THE INVENTION

As products across multiple market segments incorporate electronics withincreasing processing power, the processors & components within thoseelectronics are generating higher levels of point-source heat,potentially damaging nearby sensitive components within the products.Further, hot spots and generally the heat are objectionable to users asthey handle the devices. Current technology employs heat “spreaders” asa means to prevent heat from generating hot spots within devices. Theseare typically a very thin layer of heat-resistant material (which isalso heat conductive) placed inside the device, covering as much of thedevice footprint as possible. The spreader overlays and absorbs pointsource heat and conducts (spreads) it across its surface area, reducing“hot spots.” A heat spreader that is more effective in both absorbingand moving heat as well as isolating sensitive components is needed.

SUMMARY OF THE INVENTION

The present invention involves the use of combining a densifiedpolyimide-based foam layer with an integral traditional thin film heatspreader to improve the in-plane (XY direction) thermal conductivity ofthe heat spreader itself. This is achieved by utilizing the excellentthermal resistance of the polyimide foam material to block thethrough-plane heat flow, allowing the heat to channel through a path ofleast resistance, namely the in-plane direction. The improved thermalresistance created by the foam layer in combination with the heatspreader layer further improves the in-plane performance of atraditional isotropic heat spreader alone. The polyimide material hasexcellent thermal insulation properties and can withstand continuous useat elevated temperatures over the life of the product without thermaldegradation, making it well suited for most thermal managementapplications requiring heat shielding and spreading performance.Combining the polyimide layer with the heat spreader also provideselectrical insulation to allow the treatment to be sandwiched betweencommon electronic components (like Printed Circuit Board Assembliesand/or displays). This solution combines both thermal protection as wellas mechanical shock fortification due to its physical properties ascellular foam.

By adding a thin layer of polyimide foam thermal insulating material toa traditional heat spreader, a significant improvement is realized inheat shielding and spreading performance over the traditional product.The insulating material being proposed is densified polyimide foam.Polyimides are well-known as one of the highest thermal stabilitypolymer classes and the foam configuration affords excellent thermalresistivity. Moreover, the polyimide foam offers approximately 4× thethermal resistance than polyimide film alone.

The present invention is well suited for any electronic device thatpossesses both heat generating electrical components in very closeproximity with heat sensitive components (like display screens orbatteries), particularly in small form factor or sealed devices in whichtraditional convection type cooling is not possible or practical, andheat spreader devices are commonly used to conduct heat away from andshield critical components from concentrated heat sources. This includescommon consumer electronic devices like mobile phones, tablets andcomputers, televisions, home appliances, set-top boxes (residentialcommunication), aviation or automotive instrumentation, oraudio/infotainment devices. Due to the different size and shape ofcomponents on the circuit board, select areas can be further densifiedto accommodate the various elevations and thicknesses.

BRIEF DESCRIPTION OF THE DRAWINGS

A preferred embodiment of this invention has been chosen wherein:

FIG. 1 is a side view of the treatment as installed in a mobile device;

FIG. 2 is a side view of the treatment in FIG. 1 as used in a differentmobile device;

FIG. 3 is a side view of one embodiment of the treatment using apressure sensitive layer to adhere to the heat generating components;

FIG. 4 is a side view of an embodiment of the treatment having a foillayer for EMI shielding;

FIG. 5 is a side view of another embodiment of the treatment using anon-conductive layer to overlay the heat generating components;

FIG. 6 is a side view of the embodiment shown in FIG. 3 using selectivepressure sensitive areas;

FIG. 7 is a side view of the treatment using selective pressuresensitive areas and a non-conductive layer to overlay the heatgenerating components;

FIG. 8 is a side view of the treatment shown in FIG. 3 with anon-conductive layer to overlay the heat sensitive components;

FIG. 9 is an exploded isometric view of the embodiment in FIG. 4 usingselective pressure sensitive areas;

FIG. 10 is an exploded isometric view of a mobile device using thetreatment with further densified areas;

FIG. 11 is a side view of section 11-11 of the device in FIG. 10; and

FIG. 12 is a partial view 12 of the section shown in FIG. 11.

DESCRIPTION OF THE PREFERRED EMBODIMENT

The treatment 10, shown in all FIGS, both insulates and spreads heat. Itis created by combining a thin layer of thermal insulating material 12to a traditional heat spreader treatment 14. The heat spreader 14 iscommonly graphite based or other thermally conductive material likemetal foil. The heat shielding and spreading performance will beimproved, better protecting sensitive components 16 of typical consumerelectronic products (such as OLED displays). The insulating material 12is a unique and novel version of densified polyimide foam. The treatment10 consists of the lamination of a thin, foamed polyimide-based layer ofinsulating material 12 to typical heat spreader treatments 14, either tohighly conductive graphite based spreader materials, or more commonmetal foil spreaders like copper or aluminum.

The treatment 10 is intended for applications where small gaps (i.e.0.25 to 5 mm) exist between a heat source such as a heat source 18 orbattery 19 and heat sensitive components such as screen 16 that istypical of small form factor devices. As shown in FIG. 10, the heatsources 18 frequently are mounted to a circuit board 26 to makeelectrical connections. Heat sources 18 and batteries 19 rely onradiated heat to maintain internal temperatures. This is the case insealed electronic devices 20 where it is impractical or impossible touse forced air cooling techniques. Therefore, graphite or foil based XYplane heat spreaders 14 are commonly used to conduct heat away from heatsensitive components 16 (when heat spreader 14 is attached to heatsource 18), or act as heat shield for heat sensitive components 16 orthe user, which typically touches the outside surface 22 of a top glass24. The insulating layer 12 has the added benefit of providingelectrical insulation of the heat spreader 14 to the heat sensitivecomponents 16 (either an unsealed graphite, or metal foil type)preventing short circuit between adjacent electrical components.

The insulating layer 12 offers the benefit of improved thermal stabilityand resistance at elevated service temperatures without degradation overtime, and low thermal conductivity compared to other plastic based filmsor foam layers. A foamed version of the polyimide material offersimproved thermal resistance due to its unique foaming process thatproduces pockets that further reduce thermal conductivity by as much as4× when compared to traditional polyimide (cast, blown or extruded) filmmaterial (typically from 0.12 W/mK to 0.043-0.049 W/mK). These cells canbe either open or closed, depending on the process used to create them.The insulating layer 12 can be very thin (<0.05 mm) or very thick (>10mm) depending on the requirements of the application.

Solimide polyimide based cellular foam is well established as anexcellent thermal insulating material 12 with thermal conductivityvalues in the order of 0.039-0.046 W/mK. The material can further be“densified” through the process of applying heat and pressure collapsingthe foam into a much thinner layer of increased density and improvingthe insulating properties by as much as ⅓. Densification can be appliedto the foam to compress from a typical foamed density of ˜0.4lbs./cu.ft. to a range from 1 to 10 lbs./cu.ft. while maintaining orreducing the thermal conductivity (i.e. as much as 30% when compressedto 2 to 3 lbs./cu.ft. range). Densification produces a thinnerinsulating layer (0.25 to 2 mm) that would otherwise be difficult toskive using traditional slitting equipment (>2 mm). The thinner, denserfoam retains much of its same cellular properties while being bettersuited to fit within the smaller form factor of typical consumerelectronic devices. Depending on the final thickness of the insulatingmaterial desired, the material may be skived before or afterdensification. The thinnest final thickness commonly requires skivingbefore densification.

Exploded side views of several variants of treatment 10 are shown inFIGS. 3-9. The densified foam is an insulating layer 12 which has anadhesive facing surface 30 and an oppositely located outside facingsurface 32. The distance between these surfaces 30,32 determines thethickness of the insulating layer 12. The treatment 10 can have a rangeof embodiments, some of which are shown in FIGS. 3-8. All of theembodiments of the treatment 10 have the insulating layer 12 bonded to aheat spreader 14 using a pressure sensitive adhesive layer 40. Thepressure sensitive adhesive layer 40 is typically as thin as possible.For example, a thickness of 0.01 mm to 0.1 mm is common, but otherthicknesses are contemplated.

The heat spreader 14 can be either a foil or graphite based material.Metal foil (typically aluminum or copper) has isotropic heat transferproperties, meaning that the heat transferred travels in all directionsequally as it is applied at a specific point. Graphite is typicallyflexible but can be rigid, depending on the manufacturing processingused. Natural graphite, which is made of graphite flake, which has been“exfoliated” through a chemical and thermal reaction, then consolidatedand compressed to rolls of spreader media. Synthetic or “Pyrolytic”graphite is commonly made from taking rolls of polyimide film which hasbeen carbonized in an oven at temperatures approaching 2000 degrees C.then calendared down to thickness. Graphite, as a heat spreader 14, iscommonly formulated to have anisotropic heat transfer properties. Thetypical heat transfer property in graphite heat spreaders 14 is highlyconductive in-plane and is resistant to heat transfer through-plane. Asdescribed, it is a relatively thin sheet of material with two surfaces.Isotropic and anisotropic heat transfer properties are well known in theart. A component facing surface 34 and an adhesive facing surface 36define the thickness of the heat spreader 14. A thin layer thateffectively spreads heat is the most desirable property for the heatspreader 14. For a heat spreader 14 with anisotropic properties, thereis a primary direction where heat travels along the plane of thematerial, but it is only a preferential heat transfer direction and someheat transfers through the thickness of the material.

As shown in FIG. 3, the treatment 10 is made when the insulating layer12 is permanently laminated to the heat spreader 14 using a thinpressure sensitive adhesive layer 40, creating a large sheet orcontinuous roll material that can be converted into a final part shapeas a full construction. By combining the heat spreader 14 and theinsulating layer 12, heat is drawn away from a heat source 18 on oneside while heat sensitive components 16 located on the other side areshielded from adjacent heated areas. To make the treatment 10 morerobust, easier to handle, cut, and install, it is necessary topermanently bond the heat spreader 14 to the insulating layer 12. Thisis accomplished through the pressure sensitive adhesive layer 40 asshown in FIGS. 3-9. The pressure sensitive adhesive layer 40, as shown,resides between the heat spreader 14 and the insulating foam layer 12.The pressure sensitive adhesive layer 40 has a first adhesive surface 42and an oppositely located second adhesive surface 44. The purpose ofthis pressure sensitive adhesive layer 40 is to permanently bond theheat spreader 14 to the insulating layer 12. It is contemplated that thepressure sensitive adhesive layer 40 has some form of reinforcement,such as fiberglass strand or other material that reduces the ability ofthe material to be torn or stretched. The pressure sensitive adhesivelayer 40, the insulating layer 12, and the heat spreader 14 are made asthin as possible while still effectively insulating and spreadingunwanted heat. This is especially important when the material is usedwith compact mobile electronics, where space is a premium.

Several embodiments include a second pressure sensitive adhesive layer46 that can be added when the treatment 10 is affixed to a device 20.The second pressure sensitive adhesive layer as described is shown inFIGS. 3, 4, and 8. The second pressure sensitive adhesive layer 46 has afirst surface 48 and an oppositely located second surface 50. The firstsurface 48 has an adhesive coating that will adhere to the componentfacing surface 34 of the heat spreading material 14. The second pressuresensitive adhesive layer 46 also can serve as an electrical insulator ifthe material 10 overlays a circuit board with conductive portions thatmay be shorted if the heat spreader 14 directly contacted thoseportions. It is common that the second pressure sensitive adhesive layer46 can be made from a thin material with dielectric properties (such aspolyester, polyimide film, PET, or other material) to improve theelectrical insulating properties when affixed to device 20. It isfurther contemplated that the second surface 50 has an adhesive coating(either fully covering surface 50 or selectively placed against surface50) to allow it to be permanently adhered to a circuit board or otherselective heat generating components.

The embodiment of the treatment 10 may include an electrical shield 15,typically for blocking electromagnetic radiation or interference (EMI).This embodiment is shown in FIG. 4. The electrical shield 15 may becopper foil, aluminum foil, mesh, screen, fabric, or other material thatblocks radiation and interference. The shield 15 could also be a ferriteor magnetic based layer. The electrical shield 15 may necessitate anadditional pressure sensitive adhesive layer 40, shown in FIG. 4.Another embodiment is shown in FIG. 5 that uses a dielectric layer 43that is adhered to the heat spreader 14. The dielectric layer 43 istypically a thin material with dielectric properties (such as polyester,polyimide film, PET, or other material). The commonly used dielectricfilms used are blown or extruded plastic films like PET, PI, PP, LDPE,HDPE, and TPU. The dielectric layer 43 does not have an exposed adhesivesurface that would allow the treatment 10 to adhere to the heat source18. This is useful when the treatment 10 is adjacent to a component thatwould be removable, such as a battery 19. Another embodiment of thetreatment 10 is shown in FIG. 6 where the pressure sensitive layer 47has gaps. This is useful when portions of the treatment 10 would need toadhere to certain components but not other components adjacent to them.FIG. 7 shows a combination of the dielectric layer 43 and pressuresensitive layer 47. FIG. 8 shows the treatment 10 that further includesa dielectric layer 39 that overlays the insulating layer 12. Thedielectric layer 39 is typically a thin material with dielectricproperties (such as polyester, polyimide film, PET, or other material).The dielectric layer 39 in this embodiment is roughly 10 microns thick,but other thicknesses are contemplated.

As shown in FIG. 10, due to packaging constraints the treatment 10 mayhave further densified areas 38 where the insulating layer 12 is furthercompressed to a smaller thickness. For the embodiment of the treatment10 with further densified areas 38, the additional densification mayoccur before the layers are combined or after. The further densifiedareas 38 retain most of the heat conductive and insulating propertiesbut allow for taller components. FIG. 11 shows the treatment 10 in FIG.3 as part of a device 20 with the further densified areas 38.

The individual layers that make up the treatment 10 each have a definedthickness that is consistent. One exception is where the insulatinglayer 12 has further densified areas 38. The insulating layer 12 andheat spreader 14 make up a majority of the thickness of the treatment10. The pressure sensitive adhesive layers 40, 46 and dielectric layer39, 43 are typically very thin comparatively.

The following examples and test setups are merely illustrative and donot limit this disclosure in any way. A summary of testing and thermalperformance of the treatment 10 is described hereinafter in which arepresentative thermal case study was created. The study used a testsetup which involved a circuit board with embedded heat sources and asimulated display layer where temperature is measured using an array ofthermocouples. Temperature of the heat sources and display layer weremonitored for a transient thermal event in which 2.56 W of thermal powerwas applied to heat sources through (3)×1876 Ohm resistors at 40 VDC for15 m14inute cycle. A temperature vs. time test was performed withvarious combinations of heat spreader 14 and insulating layer 12combinations. Details of the tests performed and the results are below.

The test setup was devised to help demonstrate the benefits of the aboveconcept in a generic, non-product specific manner, but intended toreplicate the typical environment of a consumer electronic product 20like a laptop, tablet or smart phone. A F4 prototype PC board 102 (80mm×110 mm×1.5 mm thick.) was used as the base structure, and three (3)1.8 kΩ resistors were bonded to the underside of the board at arbitrarylocations to simulate concentrated heat sources. The air cavity underthe board was filled with a 1″ thick layer of insulating foam to preventexternal environmental factors from influencing test results.

The resistors were powered in parallel by a regulated DC power sourcecapable of 0-50 Vdc output. The current draw to all three resistors wasmonitored. Thermocouples were embedded at each resistor location tomonitor point source temperatures. Individual potentiometers were usedto fine adjust the voltage to each resistor to achieve a desiredtemperature. For the test results presented below, a target temperatureof 75 C for each heat source was selected. An input voltage of 40 Vdcwas set on the power supply then each potentiometer was adjusted toachieve the target temperature. After a minimum dwell time of 15minutes, the temperatures of the resistors reached a steady-statecondition of 75 C with the PC board.

To simulate the heat sensitive component 16 being protected by thetreatment 10 (i.e. OLED display), a 0.010″ thick aluminum plate (100mm×120 mm) was mounted parallel to the board at fixed distance above thePCB (either 0.5 or 1.0 mm). A grid of twelve (12) flush mountedthermocouples were mounted to the top surface of the aluminum plate asshown in FIG. 8. The following temperature readings were recorded as afunction of time: (3) reference T/C's at point sources R1, R2, R3; (12)output T/C measurement grid on aluminum display plate; (1) T/C at centerpoint of display plate.

The basic test event was intended to record the transient temperaturerise from powering the heat sources from an ambient condition (˜22 C)for 1000 sec. duration. Minimum 15 minute dwell time betweenmeasurements was used to ensure the test device returned to ambienttemperature. Once resistors were set to achieve desired temperature, nochanges to the individual potentiometers or input voltage were made forthe balance of the testing. Several repeat experiments were conducted toestablish consistency of the test setup and results.

The test specimen consisted of a 65 mm×98 mm sample placed and centeredon the top side of the PC board. The basic samples consisted of a 0.025mm thick synthetic graphite heat spreader material 14 (i.e. 1500 W/mK)bonded to either a 0.5 mm or 1.0 mm thick insulating foam layer 12. Thebase foam used was Solimide HT-340 polyimide foam at 0.4 pcf (or poundsper cubic foot) starting density that was then compressed to either 0.5mm or 1.0 mm thick from a specified starting thickness to achieve thedesired final density. Various foam density values were investigated(from 2 to 10 pcf). The layup consisted of a thin PET backing film+thinbonding PSA layer 46+graphite heat layer 14+thin bonding PSA layer40+insulating foam 12. The graphite layer was placed against the heatsource (PCB) while the insulating foam layer was against the bottom sideof the 10 mil aluminum display plate 106.

Two control experiments were also performed: 1) replacing the densifiedpolyimide foam with a more thermally conductive (2X) polyurethane foam;2) removing the insulating layer using only the graphite heat spreader14 with a 1 mm air gap between the display plate and heat spreader 14.In all three cases (invention concept vs. control cases), only a slightreduction in the surface temperature of the display plate was observed(<1 C). The chief difference was the impact the treatment had on thereference temperatures of the heat sources 18. Using the case of the 1mm air gap as the untreated, baseline, the graphite+air gap controlsample increased the average resistor temperature by +2.4 C, while thegraphite+PU foam case showed a −0.9 C drop. However, for the case of thegraphite+Solimide foam, an 8.5 C temperature drop was observed. Thesetests were repeated and the findings were consistent.

Typical results demonstrate the change in average resistor temperaturevs. time for the different configurations as an indication of the heatspreading performance. Though only a small reduction in temperature wasobserved, the more interesting result is the larger reduction of heatsource temperature when using the polyimide insulating layer 12 vs. heatspreader 14 only w/ an air gap. The additional 8.5 ° C. drop intemperature comes with no change in the electrical input voltage orcurrent to the heat sources, implying that the heat spreader 14 performsbetter when backed with the polyimide insulating layer 12.

It is understood that while certain aspects of the disclosed subjectmatter have been shown and described, the disclosed subject matter isnot limited thereto and encompasses various other embodiments andaspects. No specific limitation with respect to the specific embodimentsdisclosed herein is intended or should be inferred. Modifications may bemade to the disclosed subject matter as set forth in the followingclaims.

What is claimed is:
 1. A heat spreading and insulating material for usewith a mobile device having heat generating components and heatsensitive components, said material comprising: a unitary thermalinsulating layer formed from a densified sheet of polyimide open cellfoam, said densified sheet having a first density between 25-60 kg/m³,said densified sheet having an outwardly facing surface and anoppositely located inwardly facing surface, said outwardly facingsurface being spaced from said inwardly facing surface to define a firstthickness; said unitary thermal insulating layer having furtherdensified areas where said insulating layer is further densified to havea density greater than said first density, said outwardly facing surfaceis spaced from said inwardly facing surface to define a second thicknessin said further densified areas, said second thickness in said furtherdensified areas being smaller than said first thickness; a firstadhesive layer having a first adhesive surface and an oppositely locatedsecond adhesive surface, said inwardly facing surface of said insulatinglayer adheredly contacting said first adhesive surface, said firstadhesive layer conforming to said inwardly facing surface; a heatspreading layer formed from a material that conducts heat and having anadhesive facing surface and an oppositely located component facingsurface, said adhesive facing surface separated from said componentfacing surface to define a thickness, said adhesive facing surfaceadheredly contacting said second adhesive surface of said first adhesivelayer, said heat spreading layer conforming to said second adhesivesurface; and an electrically insulating layer adhered to said componentfacing surface of said heat spreading layer.
 2. The heat spreadingmaterial of claim 1, when said heat spreading layer is adjacent saidheat generating components, heat from said heat generating componentspreferentially transfers along said thickness of said heat spreadinglayer.
 3. The heat spreading material of claim 1, wherein saidelectrically insulating layer has an exposed adhesive surface to form asecond pressure sensitive adhesive layer, said second pressure sensitiveadhesive layer in contact with said heat generating components.
 4. Theheat spreading material of claim 3, wherein said second pressuresensitive adhesive layer has gaps in said exposed adhesive surface. 5.The heat spreading material of claim 1, when said heat spreading layercontacts said heat generating components, heat from said heat generatingcomponents preferentially transfers along said thickness of said heatspreading layer.
 6. A heat spreading and insulating material for usewith a mobile device having heat generating components and heatsensitive components, said material comprising: a unitary thermalinsulating layer formed from a densified sheet of polyimide open cellfoam, said densified sheet having a first density between 25-60 kg/m³,said densified sheet having an outwardly facing surface and anoppositely located inwardly facing surface, said outwardly facingsurface being spaced from said inwardly facing surface to define a firstthickness; said unitary thermal insulating layer having furtherdensified areas where said insulating layer is further densified to havea density greater than said first density, said outwardly facing surfaceis spaced from said inwardly facing surface to define a second thicknessin said further densified areas, said second thickness in said furtherdensified areas being smaller than said first thickness; a firstadhesive layer having a first adhesive surface and an oppositely locatedsecond adhesive surface, said inwardly facing surface of said insulatinglayer adheredly contacting said first adhesive surface, said firstadhesive layer conforming to said inwardly facing surface; and a heatspreading layer formed from a material that conducts heat and having anadhesive facing surface and an oppositely located component facingsurface, said adhesive facing surface separated from said componentfacing surface to define a thickness, said adhesive facing surfaceadheredly contacting said second adhesive surface of said first adhesivelayer, said heat spreading layer conforming to said second adhesivesurface.
 7. The heat spreading material of claim 6, further comprisingan electrically insulating layer adhered to said component facingsurface of said heat spreading layer,
 8. The heat spreading material ofclaim 7, wherein said second pressure sensitive adhesive layer is incontact with said heat generating components.
 9. The heat spreadingmaterial of claim 7, when said heat spreading layer is adjacent saidheat generating components, heat from said heat generating componentspreferentially transfers along said thickness of said heat spreadinglayer.
 10. The heat spreading material of claim 7, wherein saidelectrically insulating layer has an exposed adhesive surface to form asecond pressure sensitive adhesive layer.
 11. The heat spreadingmaterial of claim 10, wherein said electrically insulating layer hasgaps in said exposed adhesive surface.